| Diameter Tolerance, mm: |
+ 0,00 , - 0,12 |
| Thickness Tolerance, mm: |
± 0,25 |
| Wavelength, nm: |
257 |
| Subtrate Material: |
UV FS |
| Angle of Incidence (AOI): |
0° |
| Coated Surface Flatness: |
λ/8 at 633 nm over 80% of diameter |
| S1 Surface Flatness: |
λ/10 typical at 633 nm |
| S1 Surface Quality: |
20-10 scratch & dig (MIL-PRF-13830B) |
| S2 Surface Quality: |
Commercial polish |
| Wedge: |
< 3 minutes |
| Chamfer: |
0,3 mm at 45° typical |
| Technology: |
Ion Beam Sputtering (IBS) |
| Adhesion and Durability: |
Per MIL-C-675A. Insoluble in lab solvents |
| Laser Induced Damage Threshold (LIDT): |
>0,3 J/cm² |
| Clear Aperture: |
Exceeds central 85% of diameter |
| Size, mm: |
12,7 x 6 |
| R, % (s+p)/2: |
99.50% |
| Csoportkésleltetési diszperzió: |
|GDD| < 30 fs2 |
| Notes: |
Névleges hullámhosszon mérve, 50 ns-os impulzus, 100 Hz |
| Főkategória: |
Optical Components |
| Alkategória1: |
Dielectric Mirrors |
| Alkategória2: |
Nagy teljesítményű lézertükrök femtoszekundumos alkalmazásokhoz |